CN113258083B - Co X Bifunctional catalyst with P nanoparticles embedded with nitrogen and phosphorus doped carbon and preparation method and application thereof - Google Patents
Co X Bifunctional catalyst with P nanoparticles embedded with nitrogen and phosphorus doped carbon and preparation method and application thereof Download PDFInfo
- Publication number
- CN113258083B CN113258083B CN202110313747.2A CN202110313747A CN113258083B CN 113258083 B CN113258083 B CN 113258083B CN 202110313747 A CN202110313747 A CN 202110313747A CN 113258083 B CN113258083 B CN 113258083B
- Authority
- CN
- China
- Prior art keywords
- catalyst
- nitrogen
- cop
- zif
- mpsa
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention belongs to the field of electrocatalysis, and relates to Co X The P nanoparticles are embedded in a bifunctional catalyst of nitrogen and phosphorus doped carbon. The invention carries out controllable synthesis of Co by adjusting the proportion of the precursors ZIF-67 and MPSA 2 P、Co 2 The bifunctional catalyst with P/CoP and CoP nanoparticles embedded in nitrogen and phosphorus doped carbon has excellent ORR/OER catalytic activity and stability. The composite catalyst with the Co-based transition metal phosphide embedded with the heteroatom doped carbon is prepared by a simple and environment-friendly one-step carbonization method, and meanwhile, the method can also be suitable for preparing other bifunctional catalysts with the heteroatom doped carbon derived from the transition metal phosphide.
Description
Technical Field
The invention belongs to the field of electrocatalysis, and relates to Co X The P nanoparticles are embedded in a bifunctional catalyst of nitrogen and phosphorus doped carbon.
Background
The zinc-air battery has the advantages of high theoretical energy density, low price, good safety and the like, and in recent years, the zinc-air battery has attracted wide attention on portable electronic equipment and electric automobiles. However, the lack of efficient and stable Oxygen Reduction Reaction (ORR) and Oxygen Evolution Reaction (OER) dual-function catalysts has limited the development and commercial application of rechargeable zinc-air batteries. At present, Pt-based catalysts and Ir/Ru-based catalysts are ORR catalysts and OER catalysts with higher efficiency respectively. However, the noble metal catalyst has the problems of resource scarcity, high price, poor stability, poor bifunctional performance and the like. In order to further promote the development of zinc-air batteries and realize commercial application, research and development of efficient and stable ORR/OER bifunctional catalysts are urgently needed.
Transition Metal Phosphides (TMPs), including Fe, Co, Cu, Ni, etc., have excellent physicochemical properties, a diversified synthesis method, and good OER catalytic activity, etc., and in recent years, the transition metal phosphides have received much attention. ORR and OER are a pair of reversible reactions, the reaction paths are different, and the corresponding catalytic sites are different, so that the transition metal phosphide with a single active site can not effectively catalyze the ORR and OER reactions at the same time.
Chinese patent application document (application No. CN201810922115.4) discloses a phosphorus-doped porous carbon-coated cobaltosic oxide oxygen reduction catalyst, and a preparation method and application thereof, wherein a phosphorus-doped porous carbon-coated cobaltosic oxide pro-catalyst Co is prepared by taking ZIF-67 with a porous structure as a template and a precursor and taking sodium phytate as a P source 3 O 4 Catalyst Co prepared from/PPC, but with P only doped and no phosphating of the metal 3 O 4 the/PPC only shows ORR catalytic activity.
Disclosure of Invention
The invention aims to solve the problems in the prior art and provides Co with simple preparation method and excellent catalytic activity and stability X The P nanoparticles are embedded in a bifunctional catalyst of nitrogen and phosphorus doped carbon.
The purpose of the invention can be realized by the following technical scheme:
co X Bifunctional catalyst with P nanoparticles intercalated with nitrogen and phosphorus doped carbon, Co X P nanoparticles are Co 2 One or both of P and CoP.
CoP and Co 2 P is both an active species of ORR and/or OER. By preparing cobalt phosphide with different stoichiometric ratios, investigating the electrocatalytic performance of phosphide with different stoichiometric ratios to ORR/OER,has important significance for preparing the bifunctional catalyst of Co-based metal phosphide, and the preparation and synthesis of the invention respectively use Co 2 P、Co 2 The P/CoP and CoP nano-particle embedded N, P carbon-doped bifunctional catalyst shows excellent ORR/OER catalytic activity.
Co X A method for preparing a bifunctional catalyst with P nanoparticles embedded in nitrogen and phosphorus doped carbon, said method comprising the steps of: mixing and grinding ZIF-67 and MPSA, and then carbonizing at high temperature in nitrogen to obtain the catalyst.
In one of the above-mentioned Co X In the preparation method of the bifunctional catalyst with the P nanoparticles embedded in nitrogen and phosphorus doped carbon, the mass ratio of ZIF-67 to MPSA is 1: (0.5-1.5).
MPSA is a macromolecular polymer obtained by polymerizing phytic acid and melamine, and the content of MPSA is increased, so that the content of P is increased, and the increased content of P can lead to Co 2 P transitions to CoP. When the mass ratio of ZIF-67 to MPSA is 1: 0.5, the catalyst contains Co nanoparticles 2 The form of P exists; when the mass ratio of ZIF-67 to MPSA is 1: 1 hour, Co 2 Partial transition of P to CoP, so that the nanoparticles in the catalyst are Co 2 The form of P/CoP exists; when the mass ratio of ZIF-67 to MPSA is 1: 1.5 times, Co 2 P is completely converted into CoP, so that the nanoparticles in the catalyst exist in the form of CoP. The method prepares and synthesizes Co respectively by adjusting the mass ratio of ZIF-67 to MPSA 2 P、Co 2 The P/CoP and CoP nano-particle embedded N, P carbon-doped bifunctional catalyst shows excellent ORR/OER catalytic activity and excellent cycle charge and discharge stability when used as an air electrode of a zinc-air battery.
In one of the above-mentioned Co X In the preparation method of the bifunctional catalyst with the P nano particles embedded with nitrogen and phosphorus doped with carbon, the preparation method of the ZIF-67 comprises the following steps: firstly, respectively dissolving cobalt nitrate hexahydrate and dimethylimidazole in methanol to form a solution, then mixing the cobalt nitrate hexahydrate and the dimethylimidazole to form a turbid liquid, standing to obtain a precipitate, centrifuging and washing the precipitate, then washing with methanol, and finally drying to obtain the ZIF-67.
In one of the above-mentioned Co X P nanoparticlesIn the preparation method of the bifunctional catalyst with particles embedded with nitrogen and phosphorus doped with carbon, the preparation method of MPSA comprises the following steps: dissolving melamine in deionized water, adding phytic acid solution after the melamine is completely dissolved, stirring and filtering to obtain a solid product, and finally performing freeze drying to obtain MPSA.
In one of the above-mentioned Co X In the preparation method of the bifunctional catalyst with the P nano-particles embedded with nitrogen and phosphorus doped carbon, the concentration of the phytic acid solution is 65-75%.
In one of the above-mentioned Co X In the preparation method of the bifunctional catalyst with P nano particles embedded with nitrogen and phosphorus doped with carbon, the mass ratio of melamine to phytic acid is 3 (4-5).
In one of the above-mentioned Co X In the preparation method of the bifunctional catalyst with the P nano particles embedded with nitrogen and phosphorus doped with carbon, the temperature is raised to 850-950 ℃ at the heating rate of 3-8 ℃/min, and the temperature is kept for 2-3h and then cooled to room temperature along with the furnace. Different carbonization temperatures can affect the elemental content, morphology and structure of the catalyst, and thus the final catalytic performance.
Co X The application of the bifunctional catalyst with P nanoparticles embedded with nitrogen and phosphorus doped with carbon in a rechargeable zinc-air battery comprises the steps of firstly dispersing the catalyst in a mixed solvent formed by absolute ethyl alcohol and Nafion, then carrying out ultrasonic dispersion to form ink, dripping the ink on hydrophobic carbon cloth, and drying to form a working electrode. The working electrode is used as an air electrode, the zinc sheet is used as a negative electrode, 6M KOH and 0.2M zinc acetate are used as electrolyte, and a zinc-air battery mould is adopted for assembly, so that the performance detection can be carried out.
In one of the above-mentioned Co X In the application of the bifunctional catalyst with P nanoparticles embedded into nitrogen and phosphorus doped carbon in the rechargeable zinc-air battery, the volume ratio of Nafion solution to absolute ethyl alcohol in a mixed solvent is 1: (10-12), the concentration of the Nafion solution is 5-8%.
Compared with the prior art, the invention has the following beneficial effects:
(1) the invention carries out controllable synthesis of Co by adjusting the proportion of the precursors ZIF-67 and MPSA 2 P、Co 2 Double work of embedding P/CoP and CoP nano-particles into nitrogen and phosphorus doped carbonThe catalyst has excellent ORR/OER catalytic activity and stability.
(2) The invention prepares the Co-based transition metal phosphide embedded heteroatom-doped carbon composite catalyst by a simple and environment-friendly one-step carbonization method, and meanwhile, the method can also be suitable for preparing other heteroatom-doped carbon bifunctional catalysts derived from transition metal phosphide.
(3) Co prepared by the invention 2 P@NPC、CoP@NPC、Co 2 The P/CoP @ NPC catalyst is assembled in a zinc-air cell as a catalytic layer of the zinc-air cell, such that the zinc-air cell maintains excellent cycling stability during long-term charge and discharge cycles.
Drawings
FIG. 1 is a schematic diagram of catalysts prepared in examples 1-3 and comparative example 1;
FIG. 2 shows Co obtained in example 1 of the present invention 2 X-ray diffraction (XRD) pattern of P @ NPC catalyst;
FIG. 3 shows Co obtained in example 1 2 Scanning Electron Microscope (SEM) images of the P @ NPC catalyst at different magnifications; (a) SEM pictures at low magnification; (b) SEM pictures at high magnification;
FIG. 4 shows Co obtained in example 1 2 Transmission Electron Micrograph (TEM) of P @ NPC catalyst; (a) co 2 TEM image at low magnification of P @ NPC; (b) co 2 A high resolution transmission plot of P @ C nanoparticles;
FIG. 5 shows Co obtained in example 1 2 An energy spectrum (EDS) diagram of a transmission electron micrograph of the P @ NPC catalyst, wherein (a), (b), (c) and (d) are C, N, Co and energy spectrums of P element distribution in sequence;
FIG. 6 shows Co obtained in example 1 2 An X-ray photoelectron spectroscopy (XPS) plot of the P @ NPC catalyst; (a) a full spectrogram; (b) c1 s fine spectrum; (c) n1 s fine spectrum; (d) P2P fine spectra; (e) a Co 2p fine spectrum;
FIG. 7 shows Co obtained in example 1 2 A nitrogen adsorption and desorption curve and a pore size distribution diagram of the P @ NPC catalyst; (a) a nitrogen adsorption and desorption curve; (b) pore size distribution curve;
FIG. 8 shows Co obtained in example 2 of the present invention 2 X-ray diffraction (XR) of P/CoP @ NPC catalystD) A drawing;
FIG. 9 shows Co obtained in example 2 2 Scanning Electron Microscope (SEM) image of P/CoP @ NPC catalyst; (a) SEM images at low magnification; (b) SEM images at high magnification;
FIG. 10 shows Co obtained in example 2 2 Transmission Electron Micrograph (TEM) of P/CoP @ NPC catalyst; (a) low power TEM images; (b) co 2 P nano-particle high resolution map; (c) CoP, Co 2 A high resolution TEM image of the P nanoparticles; (d) co 2 A P nanoparticle lattice fringe pattern; (e) a CoP nanoparticle lattice fringe pattern;
FIG. 11 shows Co obtained in example 2 2 Transmission electron micrograph (EDS) of P/CoP @ NPC catalyst; (a) c, N, P and a Co element distribution energy spectrogram are formed in sequence in the steps (b), (c) and (d);
FIG. 12 shows Co obtained in example 2 2 An X-ray photoelectron spectroscopy (XPS) plot of the P/CoP @ NPC catalyst; (a) a full spectrogram; (b) c1 s fine spectrum; (c) n1 s fine spectrum; (d) P2P fine spectrum; (e) a Co 2p fine spectrum;
FIG. 13 shows Co obtained in example 2 2 A nitrogen adsorption and desorption curve and a pore size distribution diagram of the P/CoP @ NPC catalyst; (a) a nitrogen adsorption and desorption curve; (b) an aperture distribution map;
FIG. 14 is an X-ray diffraction (XRD) pattern of the CoP @ NPC catalyst prepared in example 3;
FIG. 15 is a Scanning Electron Microscope (SEM) image of the CoP @ NPC catalyst prepared in example 3; (a) low power SEM image; (b) high power SEM image;
FIG. 16 is an X-ray photoelectron spectroscopy (XPS) plot of the CoP @ NPC catalyst prepared in example 3; (a) a full spectrogram; (b) c1 s fine spectrum; (c) n1 s fine spectrum, (d) P2P fine spectrum, (e) Co 2P fine spectrum;
FIG. 17 is a plot of the nitrogen desorption curve and pore size distribution for the CoP @ NPC catalyst prepared in example 3; (a) a nitrogen adsorption and desorption curve; (b) an aperture distribution map;
FIG. 18 is an X-ray diffraction (XRD) pattern of the Co @ NC catalyst prepared in comparative example 1;
FIG. 19 is a Scanning Electron Microscope (SEM) image of the Co @ NC catalyst prepared in comparative example 1; (a) SEM images at low magnification, (b) SEM images at high magnification;
FIG. 20 is an X-ray photoelectron spectroscopy (XPS) plot of a Co @ NC catalyst prepared in comparative example 1; (a) a full spectrogram; (b) c1 s fine spectrum; (c) n1 s fine spectrum; (d) a Co 2p fine spectrum;
FIG. 21 is a graph showing the nitrogen desorption curve and the pore size distribution of the Co @ NC catalyst prepared in comparative example 1; (a) a nitrogen adsorption and desorption curve; (b) an aperture distribution map;
FIG. 22 is a linear voltammogram of the oxygen reduction catalytic activity of the catalysts obtained in examples 1-3, comparative example 1;
FIG. 23 is a linear voltammogram of the oxygen evolution catalytic activity of the catalysts obtained in examples 1-3, comparative example 1;
FIG. 24 shows Co obtained in example 1 2 A timing current curve corresponding to the P @ NPC composite catalyst and Pt/C;
FIG. 25 shows Co obtained in example 1 2 P @ NPC composite catalyst and RuO 2 A corresponding timing voltage curve;
FIG. 26 shows Co obtained in example 1 2 P @ NPC composite catalyst and Pt/C + RuO 2 Respectively used as power density curves of the zinc-air battery corresponding to the air electrode catalyst;
FIG. 27 shows Co in example 4 2 P @ NPC is taken as a cyclic charge-discharge curve of the air electrode catalyst corresponding to the zinc-air battery;
Detailed Description
The following are specific examples of the present invention and further describe the technical solutions of the present invention, but the present invention is not limited to these examples.
Preparation of ZIF-67: dissolving 7mmol of cobalt nitrate hexahydrate in 50mL of methanol to form a solution A, dissolving 10mmol of dimethyl imidazole in 50mL of methanol to form a solution B, introducing the solution A into the solution B, and continuously stirring for 10min to form a suspension. Standing the suspension at room temperature for 24h, centrifuging and washing the formed precipitate, washing with methanol for three times, drying in an oven at 60 ℃ for 6h to obtain ZIF-67, and placing in a drying vessel for later use.
Preparation of MPSA: dissolving 0.75g of melamine into 300mL of deionized water, adding 1g of 70% phytic acid solution into the solution after the melamine is completely dissolved, stirring for 30min, carrying out suction filtration on the suspension, freeze-drying the solid product obtained by suction filtration, and drying to obtain MPSA which is put into a drying vessel for later use.
Example 1
Mixing 300mg of ZIF-67 and 150mg of MPSA, grinding to uniformly mix the ZIF-67 and the MPSA, and putting the mixture into a tube furnace for high-temperature carbonization under the protection of nitrogen: heating to 900 ℃ at the heating rate of 5 ℃/min, preserving the heat for 2h, and cooling to room temperature along with the furnace to obtain Co 2 P @ NPC catalyst.
Example 2:
mixing 300mg ZIF-67 and 300mg MPSA, grinding to uniformly mix the ZIF-67 and the MPSA, putting the mixture into a tube furnace, and performing high-temperature carbonization under the protection of nitrogen: heating to 890 ℃ at the heating rate of 4 ℃/min, preserving the temperature for 2h, and cooling to room temperature along with the furnace to obtain Co 2 P/CoP @ NPC catalyst.
Example 3:
mixing 300mg ZIF-67 and 450mg MPSA, grinding to uniformly mix the ZIF-67 and the MPSA, putting the mixture into a tube furnace, and performing high-temperature carbonization under the protection of nitrogen: heating to 910 ℃ at the heating rate of 6 ℃/min, preserving the temperature for 3h, and cooling to room temperature along with the furnace to obtain the CoP @ NPC catalyst.
Example 4:
10mg of Co prepared in example 1 were taken 2 The P @ NPC catalyst is dispersed in a mixed solvent formed by 1mL of absolute ethyl alcohol and 100 mu L of 5% nafion solution, and ultrasonic dispersion is carried out for 30min to form ink. 17 μ L of the ink was dropped onto a hydrophobic carbon cloth, and naturally dried to be used as a working electrode. The prepared working electrode is used as an air electrode, a zinc sheet is used as a negative electrode, 6M KOH and 0.2M zinc acetate are used as electrolytes, and a zinc-air battery mould assembly is adopted for testing.
Example 5:
10mg of Co prepared in example 2 were taken 2 The P/CoP @ NPC catalyst is dispersed in a mixed solvent formed by 1mL of absolute ethyl alcohol and 100 mu L of 5% nafion, and ultrasonic dispersion is carried out for 30min to form ink. Dripping 17 μ L of the above ink on hydrophobic carbon cloth, and naturally dryingUsed as an electrode. The prepared working electrode is used as an air electrode, a zinc sheet is used as a negative electrode, 6M KOH and 0.2M zinc acetate are used as electrolytes, and a zinc-air battery mould assembly is adopted for testing.
Example 6:
10mg of the CoP @ NPC catalyst prepared in example 3 was dispersed in a mixed solvent of 1mL of absolute ethanol and 100. mu.L of 5% nafion, and ultrasonically dispersed for 30min to form an ink. 17 μ L of the ink was dropped onto a hydrophobic carbon cloth, and naturally dried to be used as a working electrode. The prepared working electrode is used as an air electrode, a zinc sheet is used as a negative electrode, 6M KOH and 0.2M zinc acetate are used as electrolytes, and a zinc-air battery mould assembly is adopted for testing.
Comparative example 1:
and putting 300mg of ZIF-67 into a porcelain boat, putting the porcelain boat into a tube furnace, heating to 900 ℃ at a heating rate of 5 ℃/min under the protection of nitrogen, preserving heat at 900 ℃ for 2h, and cooling along with the furnace to obtain black powder, namely Co @ NC.
Comparative example 2:
5mg of the CoP @ NPC catalyst prepared in comparative example 1 was dispersed in a mixed solvent of 1mL of absolute ethanol and 100. mu.L of 5% nafion, and ultrasonically dispersed for 30min to form an ink. 17mL of the ink was dropped onto a hydrophobic carbon cloth, and the ink was allowed to dry naturally and used as a working electrode. The prepared working electrode is used as an air electrode, a zinc sheet is used as a negative electrode, 6M KOH and 0.2M zinc acetate are used as electrolytes, and a zinc-air battery mould assembly is adopted for testing.
FIG. 1 is a schematic diagram of the preparation of composite catalysts of examples 1 to 3 and comparative example 1, when the mass ratio of ZIF-67 to MPSA is 1: 0.5, the catalyst contains Co nanoparticles 2 The form of P exists; when the mass ratio of ZIF-67 to MPSA is 1: 1 hour, Co 2 Partial transition of P to CoP, so that the nanoparticles in the catalyst are Co 2 The form of P/CoP exists; when the mass ratio of ZIF-67 to MPSA is 1: 1.5 times, Co 2 P is completely transited to CoP, so that the nanoparticles in the catalyst exist in the form of CoP; the nanoparticles in the catalyst prepared directly by ZIF-67 were present in the form of Co.
Co prepared in example 1 2 XRD diffractogram of P @ NPC is shown in figure 2Typical Co is present in the XRD diffractogram 2 Diffraction peak of P phase, which proves that the prepared catalyst contains Co 2 And (P). FIG. 3 is Co 2 SEM images of P @ NPC at different magnifications, from which Co can be seen 2 P @ NPC is an irregular polyhedral structure, and metal particles are uniformly distributed on the irregular polyhedral structure. In FIG. 4, (a) and (b) are Co 2 TEM and HRTEM of P @ NPC, evidence of Co 2 The P nano-particles are coated in 3-4 layers of graphite carbon layers. FIG. 5 shows Co 2 EDS diagram of P @ NPC, C, N, Co and P element are uniformly distributed. FIG. 6 shows Co 2 XPS plot of P @ NPC, further demonstrating Co 2 The four elements C, N, Co and P and the elements N and P in the P @ NPC are doped into the carbon skeleton. FIG. 7 shows Co 2 The nitrogen adsorption and desorption curve and the pore size distribution diagram corresponding to the P @ NPC show that the P @ NPC is a typical mesoporous material, and a hierarchical pore structure of micropores and macropores also exists.
Example 2 Co preparation 2 The XRD diffractogram of P/CoP @ NPC is shown in FIG. 8, demonstrating Co 2 Co in P/CoP 2 Two phases, P and CoP. FIG. 9 shows Co 2 P/CoP @ NPC Scanning Electron Microscope (SEM) picture, it can be seen from the picture that the irregular polyhedral structure begins to collapse, and metal particles with uneven sizes are distributed on the spherical-like nano particles. FIG. 10 shows Co 2 TEM and HRTEM images of P/CoP @ NPC demonstrated at Co 2 P/CoP @ NPC Co-Presence 2 P nanoparticles and Co 2 P/CoP composite nanoparticles. FIG. 11 shows Co 2 EDS diagram of P/CoP @ NPC, which demonstrates C, N, P, Co that four elements are evenly distributed. FIG. 12 shows Co 2 The XPS plot of P/CoP @ NPC also confirms the presence of the 4 elements described above and the doping of the N and P elements into the carbon skeleton. FIG. 13 shows Co 2 The P/CoP @ NPC nitrogen adsorption and desorption curve and the corresponding pore size distribution diagram prove that the mesoporous material is a typical mesoporous material.
The X-ray diffraction (XRD) pattern of the CoP @ NPC prepared in example 3 is shown in FIG. 14, and a typical CoP phase diffraction peak exists in the XRD pattern, so that the CoP is contained in the prepared catalyst. FIG. 15 is an SEM image of CoP @ NPC at different magnifications, from which it can be seen that CoP @ NPC is an irregular polyhedral structure on which metal particles are uniformly distributed. FIG. 16 is an XPS plot of CoP @ NPC, further demonstrating that C, N, Co and P four elements and N and P elements are doped into the carbon skeleton in CoP @ NPC. Fig. 17 is a nitrogen adsorption/desorption curve and a pore size distribution diagram corresponding thereto, and it is confirmed that it is also a typical mesoporous material, and a hierarchical pore structure of both micropores and macropores is present.
The X-ray diffraction (XRD) pattern of the Co @ NC catalyst prepared in comparative example 1 is shown in fig. 18, demonstrating that direct carbonization of ZIF-67 forms metallic Co simple substance. The corresponding SEM images at different magnifications are shown in fig. 19, and it can be seen that Co @ NC is an irregular polyhedral structure on which metal particles are distributed. Fig. 20 is an X-ray photoelectron spectroscopy (XPS) picture corresponding to Co @ NC, where C: 1s, O: 1s, N: 1s and Co: 2p, demonstrating the presence of the element in 4 above in Co @ NC. FIG. 21 is a graph of the nitrogen desorption curve and pore size distribution of Co @ NC, which shows that Co @ NC is a typical mesoporous material.
From FIG. 22, Co can be seen 2 P @ NPC had a slightly poorer initial potential ratio than Pt/C, but its ORR catalytic activity was superior to that of the other comparative samples, where Co 2 The ORR catalytic activity of P/CoP @ NPC and CoP @ NPC is significantly reduced.
From FIG. 23, Co can be seen 2 OER catalytic activity of P/CoP @ NPC is optimal, Co 2 P @ NPC, where Co 2 The OER catalytic activity of P @ NPC is superior to that of Co 2 P @ NPC, description of Co 2 The OER intrinsic catalytic activity of P is superior to that of CoP.
From FIG. 24, Co can be seen 2 After the P @ NPC is subjected to a stability test for 20h, the current density is still maintained at 90%, and the Pt/C is reduced to 70%, indicating that Co 2 The ORR catalytic stability of P @ NPC is superior to that of Pt/C.
It can be seen from FIG. 25 that at 10mA cm -2 At a current density of (2), sample Co 2 P @ NPC was tested for 24h stability at a voltage of 1.56V to 1.60V and at a 40mV increase, versus a RuO sample 2 After 12h of test, the voltage of the material is increased by 50mV, which shows that Co 2 OER catalytic stability of P @ NPC is superior to RuO 2。
From FIG. 26, Co can be seen 2 The power density of a zinc-air battery taking P @ NPC as an air electrode catalyst is 157mW cm -2 Greater than Pt/C + RuO 2 Power Density (100mW cm) of Zinc air cell assembled as air electrode catalyst -2 )。
From FIG. 27, it can be seen that Co 2 Zinc air battery with P @ NPC as air electrode catalyst at 10mA cm -2 The current density of the battery can keep good charge-discharge cycle stability, and the charge-discharge voltage does not change obviously after 140 hours of charge-discharge cycle.
In conclusion, the invention carries out controllable synthesis on Co by adjusting the proportion of the precursors ZIF-67 and MPSA 2 P、Co 2 The bifunctional composite catalyst with the P/CoP and CoP nanoparticles embedded in nitrogen and phosphorus doped carbon has excellent ORR/OER catalytic activity and stability. When the zinc-air battery active carbon material is applied to a zinc-air battery, good cycle stability can be kept in a long-time charge-discharge cycle process, and a potential application prospect of the zinc-air battery active carbon material in a rechargeable zinc-air battery is shown.
The technical scope of the invention claimed by the embodiments of the present application is not exhaustive, and new technical solutions formed by equivalent replacement of single or multiple technical features in the technical solutions of the embodiments are also within the scope of the invention claimed by the present application; in all the embodiments of the present invention, which are listed or not listed, each parameter in the same embodiment only represents an example (i.e., a feasible embodiment) of the technical solution, and there is no strict matching and limiting relationship between the parameters, wherein the parameters may be replaced with each other without departing from the axiom and the requirements of the present invention, unless otherwise specified.
Claims (5)
1. Co X The preparation method of the bifunctional catalyst with P nano particles embedded into nitrogen and phosphorus doped carbon is characterized in that the Co nano particles are embedded into the bifunctional catalyst X P nanoparticles are Co 2 One or both of P and CoP;
the method comprises the following steps: mixing and grinding ZIF-67 and MPSA, and then carbonizing at high temperature in nitrogen to obtain a composite catalyst;
when the mass ratio of ZIF-67 to MPSA is 1: 0.5, the catalyst contains Co nanoparticles 2 The form of P exists; when the mass ratio of ZIF-67 to MPSA is 1: 1, making the nano particles in the catalyst to be Co 2 The form of P/CoP exists; when the mass ratio of ZIF-67 to MPSA is 1: 1.5, so that the nanoparticles in the catalyst exist in the form of CoP;
the preparation method of the MPSA comprises the following steps: dissolving melamine in deionized water, adding phytic acid solution after the melamine is completely dissolved, stirring and filtering to obtain a solid product, and finally performing freeze drying to obtain MPSA;
the concentration of the phytic acid solution is 65-75 percent;
the mass ratio of melamine to phytic acid is 3: (4-5).
2. Co according to claim 1 X The preparation method of the bifunctional catalyst with the P nano particles embedded with nitrogen and phosphorus doped carbon is characterized in that the preparation method of the ZIF-67 comprises the following steps: firstly, respectively dissolving cobalt nitrate hexahydrate and dimethylimidazole in methanol to form a solution, then mixing the cobalt nitrate hexahydrate and the dimethylimidazole to form a turbid liquid, standing to obtain a precipitate, centrifuging and washing the precipitate, then washing with methanol, and finally drying to obtain the ZIF-67.
3. Co according to claim 1 X The preparation method of the bifunctional catalyst with the P nano particles embedded with nitrogen and phosphorus doped with carbon is characterized in that the temperature rise rate of the high-temperature carbonization is increased to 850-950 ℃ at the speed of 3-8 ℃/min, and the temperature is kept for 2-3h and then cooled to room temperature along with the furnace.
4. Co as claimed in claim 1 X The application of the bifunctional catalyst with P nanoparticles embedded with nitrogen and phosphorus doped carbon in a rechargeable zinc-air battery is characterized in that the catalyst is dispersed in a mixed solvent formed by absolute ethyl alcohol and Nafion solution, then the catalyst is subjected to ultrasonic dispersion to form ink, the ink is dripped onto hydrophobic carbon cloth, and the working electrode is formed after the ink is dried.
5. Co according to claim 4 X The application of the bifunctional catalyst with P nanoparticles embedded into nitrogen and phosphorus doped carbon in a rechargeable zinc-air battery is characterized in that the volume ratio of Nafion solution to absolute ethyl alcohol in a mixed solvent is 1: (10-12), the concentration of the Nafion solution is 5-8%.