CN110157289A - Watersoluble plumbago alkene anticorrosive paint - Google Patents

Watersoluble plumbago alkene anticorrosive paint Download PDF

Info

Publication number
CN110157289A
CN110157289A CN201810263730.9A CN201810263730A CN110157289A CN 110157289 A CN110157289 A CN 110157289A CN 201810263730 A CN201810263730 A CN 201810263730A CN 110157289 A CN110157289 A CN 110157289A
Authority
CN
China
Prior art keywords
parts
anticorrosive paint
watersoluble plumbago
plumbago alkene
water
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201810263730.9A
Other languages
Chinese (zh)
Inventor
张成如
车春玲
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shandong Jiaxing Environmental Protection Technology Co Ltd
Original Assignee
Shandong Jiaxing Environmental Protection Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shandong Jiaxing Environmental Protection Technology Co Ltd filed Critical Shandong Jiaxing Environmental Protection Technology Co Ltd
Priority to CN201810263730.9A priority Critical patent/CN110157289A/en
Publication of CN110157289A publication Critical patent/CN110157289A/en
Pending legal-status Critical Current

Abstract

The present invention relates to a kind of watersoluble plumbago alkene anticorrosive paints, including 30~70 parts of water-base resin, 10~30 parts of graphene dispersing solution, 10~20 parts of filler, 2~8 parts of solvent, 1~6 part of defoaming agent, 10~15 parts of polytetrafluoroethylene (PTFE), six 4~8 parts of phosphorus meta-acid sodium, 1~6 part of levelling agent, 20~30 parts of curing agent, two 6~12 parts of dimethyl carbonates, 10~30 parts of deionized water.A kind of watersoluble plumbago alkene anticorrosive paint of the invention has the characteristics that energy conservation and environmental protection, adhesive force are good, water resistance is strong, antiseptic property is prominent.

Description

Watersoluble plumbago alkene anticorrosive paint
Technical field
The present invention relates to anticorrosive paint fields, and in particular to a kind of watersoluble plumbago alkene anticorrosive paint.
Background technique
As coatings industry and coating process develop to low pollutionization, water paint increasingly rises.Water paint Using pollution of the organic solvent to environment is reduced, the health of operator, safe and environment-friendly production and fortune have been ensured Transmission method receives extensive favor.But presently commercially available water-based anticorrosive paint its be difficult on Corrosion Protection and solvent type apply Material contends with, and the half of poor water resistance, salt-fog resistant time deficiency solvent based coating, this just greatly limits the development of water paint.
Summary of the invention
The purpose of the present invention is to provide a kind of watersoluble plumbago alkene anticorrosive paints, have energy conservation and environmental protection, adhesive force good, resistance to The features such as aqueous strong, antiseptic property is prominent.
A kind of watersoluble plumbago alkene anticorrosive paint, each raw material composition including following parts by weight:
30~70 parts of water-base resin, 10~30 parts of graphene dispersing solution, 10~20 parts of filler, 2~8 parts of solvent, defoaming agent 1~6 Part, 10~15 parts of polytetrafluoroethylene (PTFE), six 4~8 parts of phosphorus meta-acid sodium, 1~6 part of levelling agent, 20~30 parts of curing agent, two carbonic acid diformazans 6~12 parts of ester, 10~30 parts of deionized water.
Specifically, the water-base resin is aqueous epoxy resins, water-based acrylic resin, waterborne polyurethane resin and aqueous One of combination of inorganic resin.
Specifically, the graphene dispersing solution is that Graphene powder is added in Di(dioctylpyrophosphato) ethylene titanate Body is stirred with water dispersion.
Specifically, the filler is one of titanium dioxide, blanc fixe, ultra-fine calcite in powder or talcum powder.
Specifically, the solvent is butyl acetate or dimethylbenzene.
Specifically, the defoaming agent is polyether-modified defoaming agent.
Specifically, the levelling agent is any one of type siloxane azo polyether polyeste class, modified acroleic acid esters.
Specifically, the curing agent is water-based isocyanate curing agent.
The invention has the following advantages: a kind of watersoluble plumbago alkene anticorrosive paint of the invention, there is energy conservation and environmental protection, attached Put forth effort, the features such as water resistance is strong, antiseptic property is prominent.
Specific embodiment
Embodiment 1
A kind of watersoluble plumbago alkene anticorrosive paint, each raw material composition including following parts by weight:
30 parts of aqueous epoxy resins, 10 parts of graphene dispersing solution, 10 parts of titanium dioxide, 2 parts of butyl acetate, polyether-modified defoaming agent 1 Part, 10 parts of polytetrafluoroethylene (PTFE), six 4 parts of phosphorus meta-acid sodium, 1 part of type siloxane azo polyether polyeste class, water-based isocyanate solidification 20 parts of agent, two 6 parts of dimethyl carbonates, 10 parts of deionized water.
The graphene dispersing solution is that graphene powder and water is added in Di(dioctylpyrophosphato) ethylene titanate Dispersion is stirred.
Preparation process are as follows: water-base resin, graphene dispersing solution, filler are added plate speed in mixing kettle at 700 revs/min The lower stirring of degree 45 minutes, it is to be mixed uniformly after obtain mixture；Then solvent, defoaming agent, levelling are sequentially added into mixture Then agent adjusts revolving speed to 800 revs/min, stirs 20 minutes.Obtain uniform mixture；After all mixtures are uniform, then according to Secondary addition polytetrafluoroethylene (PTFE), six phosphorus meta-acid sodium, curing agent, two dimethyl carbonates, deionized water in mixing kettle, 600 revs/min 35 minutes are stirred under mixing speed to uniform, finally obtain watersoluble plumbago alkene anticorrosive paint.
Embodiment 2
A kind of watersoluble plumbago alkene anticorrosive paint, each raw material composition including following parts by weight:
70 parts of water-based acrylic resin, 30 parts of graphene dispersing solution, 20 parts of blanc fixe, 8 parts of dimethylbenzene, polyether-modified defoaming 6 parts of agent, 15 parts of polytetrafluoroethylene (PTFE), six 8 parts of phosphorus meta-acid sodium, 6 parts of modified acroleic acid esters, 30 parts of water-based isocyanate curing agent, Two 12 parts of dimethyl carbonates, 30 parts of deionized water.
The graphene dispersing solution is that graphene powder and water is added in Di(dioctylpyrophosphato) ethylene titanate Dispersion is stirred.
Preparation process are as follows: water-base resin, graphene dispersing solution, filler are added plate speed in mixing kettle at 600 revs/min The lower stirring of degree 40 minutes, it is to be mixed uniformly after obtain mixture；Then solvent, defoaming agent, levelling are sequentially added into mixture Then agent adjusts revolving speed to 700 revs/min, stirs 30 minutes.Obtain uniform mixture；After all mixtures are uniform, then according to Secondary addition polytetrafluoroethylene (PTFE), six phosphorus meta-acid sodium, curing agent, two dimethyl carbonates, deionized water in mixing kettle, 600 revs/min 35 minutes are stirred under mixing speed to uniform, finally obtain watersoluble plumbago alkene anticorrosive paint.
Embodiment 3
A kind of watersoluble plumbago alkene anticorrosive paint, each raw material composition including following parts by weight:
35 parts of waterborne polyurethane resin, 15 parts of graphene dispersing solution, 15 parts of ultra-fine calcite in powder is 3 parts of butyl acetate, polyether-modified 2 parts of defoaming agent, 11 parts of polytetrafluoroethylene (PTFE), six 5 parts of phosphorus meta-acid sodium, 2 parts of type siloxane azo polyether polyeste class, aqueous isocyanic acid 22 parts of ester curing agent, two 7 parts of dimethyl carbonates, 12 parts of deionized water.
The graphene dispersing solution is that graphene powder and water is added in Di(dioctylpyrophosphato) ethylene titanate Dispersion is stirred.
Preparation process are as follows: water-base resin, graphene dispersing solution, filler are added plate speed in mixing kettle at 600 revs/min The lower stirring of degree 50 minutes, it is to be mixed uniformly after obtain mixture；Then solvent, defoaming agent, levelling are sequentially added into mixture Then agent adjusts revolving speed to 700 revs/min, stirs 30 minutes.Obtain uniform mixture；After all mixtures are uniform, then according to Secondary addition polytetrafluoroethylene (PTFE), six phosphorus meta-acid sodium, curing agent, two dimethyl carbonates, deionized water in mixing kettle, 800 revs/min 35 minutes are stirred under mixing speed to uniform, finally obtain watersoluble plumbago alkene anticorrosive paint.
Embodiment 4
A kind of watersoluble plumbago alkene anticorrosive paint, each raw material composition including following parts by weight:
35 parts of aqueous inorganic resin, 25 parts of graphene dispersing solution, 18 parts of ultra-fine calcite in powder is 6 parts of butyl acetate, polyether-modified to disappear 4 parts of infusion, 13 parts of polytetrafluoroethylene (PTFE), six 7 parts of phosphorus meta-acid sodium, 5 parts of type siloxane azo polyether polyeste class, water-based isocyanate 26 parts of curing agent, two 10 parts of dimethyl carbonates, 25 parts of deionized water.
The graphene dispersing solution is that graphene powder and water is added in Di(dioctylpyrophosphato) ethylene titanate Dispersion is stirred.
Preparation process are as follows: water-base resin, graphene dispersing solution, filler are added plate speed in mixing kettle at 700 revs/min The lower stirring of degree 50 minutes, it is to be mixed uniformly after obtain mixture；Then solvent, defoaming agent, levelling are sequentially added into mixture Then agent adjusts revolving speed to 800 revs/min, stirs 30 minutes.Obtain uniform mixture；After all mixtures are uniform, then according to Secondary addition polytetrafluoroethylene (PTFE), six phosphorus meta-acid sodium, curing agent, two dimethyl carbonates, deionized water in mixing kettle, 800 revs/min 35 minutes are stirred under mixing speed to uniform, finally obtain watersoluble plumbago alkene anticorrosive paint.

Claims (8)

1. a kind of watersoluble plumbago alkene anticorrosive paint, which is characterized in that each raw material composition including following parts by weight:
30~70 parts of water-base resin, 10~30 parts of graphene dispersing solution, 10~20 parts of filler, 2~8 parts of solvent, defoaming agent 1~6 Part, 10~15 parts of polytetrafluoroethylene (PTFE), six 4~8 parts of phosphorus meta-acid sodium, 1~6 part of levelling agent, 20~30 parts of curing agent, two carbonic acid diformazans 6~12 parts of ester, 10~30 parts of deionized water.
2. a kind of watersoluble plumbago alkene anticorrosive paint according to claim 1, which is characterized in that the water-base resin is aqueous One of epoxy resin, water-based acrylic resin, waterborne polyurethane resin and combination of aqueous inorganic resin.
3. a kind of watersoluble plumbago alkene anticorrosive paint according to claim 1, which is characterized in that the graphene dispersing solution is Di(dioctylpyrophosphato) ethylene titanate is added graphene powder and stirs with water dispersion.
4. a kind of watersoluble plumbago alkene anticorrosive paint according to claim 1, which is characterized in that the filler be titanium dioxide, One of blanc fixe, ultra-fine calcite in powder or talcum powder.
5. a kind of watersoluble plumbago alkene anticorrosive paint according to claim 1, which is characterized in that the solvent is butyl acetate Or dimethylbenzene.
6. a kind of watersoluble plumbago alkene anticorrosive paint according to claim 1, which is characterized in that the defoaming agent changes for polyethers Property defoaming agent.
7. a kind of watersoluble plumbago alkene anticorrosive paint according to claim 1, which is characterized in that the levelling agent is siloxanes Any one of class azo polyether polyeste class, modified acroleic acid esters.
8. a kind of watersoluble plumbago alkene anticorrosive paint according to claim 1, which is characterized in that the curing agent is aqueous different Cyanate curing agent.
CN201810263730.9A 2018-03-28 2018-03-28 Watersoluble plumbago alkene anticorrosive paint Pending CN110157289A (en)