CN109736005A - A kind of fabric and its weaving method with damping performance - Google Patents
A kind of fabric and its weaving method with damping performance Download PDFInfo
- Publication number
- CN109736005A CN109736005A CN201910215729.3A CN201910215729A CN109736005A CN 109736005 A CN109736005 A CN 109736005A CN 201910215729 A CN201910215729 A CN 201910215729A CN 109736005 A CN109736005 A CN 109736005A
- Authority
- CN
- China
- Prior art keywords
- base fabric
- fabric
- sley bar
- mesh
- damping performance
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to textile technology fields, more particularly to a kind of fabric and its weaving method with damping performance.The present invention discloses a kind of fabric with damping performance, is the three-decker for including the first base fabric, articulamentum and the second base fabric.There is the fabric of damping performance to weave the first base fabric using sley bar GB1, GB2 and GB3, weave the second base fabric using sley bar GB4 and GB5 braiding articulamentum, using sley bar GB6 and GB7 by the present invention.Spatially waveform, the first base fabric, the second base fabric have hollow structure with intermediate connection interlayer respectively on the fabric substrate surface, have good cushion performance, and can fast quick-recovery after compressive deformation.The high resilience that fabric has can generate flexible deformation and absorb energy, have excellent damping performance in pressurized process.
Description
Technical field
The invention belongs to textile technology fields, more particularly to a kind of fabric and its weaving method with damping performance.
Background technique
Double rib warp loom can weave the three-decker fabric being made of two layers of base fabric and articulamentum.Existing three-decker
Base fabric and intermediate connecting layer including upper and lower two layers of planar structure.Intermediate connecting layer plays the role of flexible support, makes three-decker
Knitted fabric have certain shock-absorbing function.But the planar structure base fabric of existing three-decker knitted fabric is to fabric
Damping performance forms limitation.
The hollow elastic base layer of abnormity is conducive to fabric and expands deformation amplitude in loading process, increases in loading process
Area, enhance energy absorption, advantageously reduce the peak stress in stress buffering course, enhance damping performance.
In existing warp knit three-decker, intermediate connecting layer and base fabric lack elastic hollow structure, reduce in buffering course
Deformability constrains the raising of material damping performance.
Summary of the invention
The purpose of the present invention is to overcome the above shortcomings and to provide a kind of fabric and its weaving method with damping performance.
To achieve the above object, the invention is realized by the following technical scheme above-mentioned purpose: a kind of with damping performance
Fabric from top to bottom successively includes the first base fabric, articulamentum and the second base fabric;First base fabric, the second base fabric are wave-like;
The wave crest of first base fabric is located above, breakpoint joint between the trough and articulamentum of the first base fabric;Second base fabric
Wave crest is located below, breakpoint joint between the trough and articulamentum of the second base fabric;The articulamentum is high resiliency material braiding system
At.The hollow region of the arc shape formed between first base fabric and articulamentum, the second base fabric and articulamentum, makes fabric of the present invention exist
When thickness direction is by pressure, deformation occurs absorbs impact energy for the hollow region of arc shape and elastomeric articulamentum, plays good
Good absorbing shock performance.
Further, first base fabric, the wavelength of the second base fabric are equal;The wave crest and the second base fabric of first base fabric
Trough it is corresponding.Heterogeneous Permutation between first base fabric, the second base fabric, and can further be mentioned with articulamentum breakpoint joint respectively
The damping performance of high fabric of the present invention.
Further, first base fabric and the second base fabric are uniformly provided with several first mesh, several second mesh respectively;
First mesh and the second mesh are corresponding;First mesh and the second mesh are elongated shape;In the case of normality, the first net
Hole, the second mesh through to length be 0.5-0.9cm, width 0.1-0.2cm.First mesh of the first base fabric, the second base fabric
The second mesh can further improve the deformation range of the first base fabric, the second base fabric, improve the damping, buffering of fabric of the present invention
Energy.When deformation occurs, the first mesh, the length of the second mesh, width also and then change fabric, the variation adjustable range of the two
Are as follows: length adjusting range can be 0.5-0.9cm, and width adjusting range can be 0.1-0.2cm.
Further, first mesh is located at the wave crest of the first base fabric;Second mesh is located at the wave of the second base fabric
Paddy.First mesh, the corresponding setting of the second mesh, when fabric of the present invention receives impact, pressure, the first mesh, the second mesh
Deformation discovery the problems such as being consistent, the first base fabric, the second base fabric stress difference is avoided to be pullled tearing generation.
Further, the vertical range of wave crest to the trough of first base fabric, the second base fabric is 0.1-0.2cm;It is described
Articulamentum with a thickness of 0.15-0.25cm.
Within the knowledge of those skilled in the art, can also make without departing from the inventive concept of the premise
Change out, such as change fabric thickness, changes the first mesh of fabric, the length of the second mesh and pair of the first base fabric and the second base fabric
Adjusted position.
A kind of weaving of the fabric with damping performance, the fabric with damping performance is using seven sley bar
It is woven;First base fabric using sley bar GB1, sley bar GB2 and sley bar GB3 by reversely through flat lining latitude organizational composition, being compiled
It knits;The articulamentum is that variation warp sateen is mesh-structured, is woven using sley bar GB4 and sley bar GB5;Second base fabric is worn containing free
Reversed warp plain stitch, using sley bar GB6 and sley bar GB7 material knitting.
Further, described 7 is as follows the band yarn yardage and drawing-in mode of sley bar:
The band yarn number of sley bar GB1 be (0-0/2-2) * 6//, drawing-in mode be 5 skies 1 wear;
The band yarn number of sley bar GB2 be (1-0/1-2) * 6//, drawing-in mode be 5 wear 1 sky;
The band yarn number of sley bar GB3 be (1-2/1-0) * 6//, drawing-in mode be 5 wear 1 sky;
The band yarn number of sley bar GB4 be (3-4-2-1) * 8+ (3-4-1-0) * 4//, drawing-in mode be 1 wear 11 sky;
The band yarn number of sley bar GB5 is (1-0-2-3) * 8+ (1-0-3-4) * 4, and drawing-in mode is that 11 skies 1 are worn;
The band yarn number of sley bar GB6 be (1-2/1-0) * 6//* 6//, drawing-in mode be 5 wear 1 sky;
The band yarn number of sley bar GB7 be (1-2/1-0) * 6//, drawing-in mode be 5 wear 1 sky.
Fabric of the present invention passes through above-mentioned band yarn code by sley bar GB1-GB7 by the double-needle bed raschels tricot machine such as RD7-EL type
Several and drawing-in mode is weaved, and can effectively be solved in existing warp knit three-decker, intermediate connecting layer and base fabric lack in elasticity
The problem of hollow structure reduces deformability in buffering course, constrains the raising of material damping performance.
Further, the raw material of the sley bar GB1 and sley bar GB2 is POLYESTER HIGH ELASTIC YARN or polyamide fibre high stretch yarn, monofilament yarn
Fineness is 6-16tex;The sley bar GB3 raw material is POLYESTER HIGH ELASTIC YARN, and monofilament yarn fineness is 11.1-22.3tex.
Further, the raw material of the sley bar GB4 and sley bar GB5 is POLYESTER HIGH ELASTIC YARN or polyamide fibre high stretch yarn, monofilament yarn
Line fineness is 11.1-22.3tex.
Further, the raw material of the sley bar GB6 and sley bar GB7 is polyester monofilament, and the fineness of monofilament yarn is 6-
16tex。
Different monofilament yarns is respectively adopted in first base fabric, articulamentum, the second base fabric, by fabric made of braiding
Interbed: articulamentum has high resilience, and the reply shrinkage stress after deformation makes the first base fabric and the second base fabric after compressive deformation
It can fast quick-recovery.
By using above-mentioned technical proposal, the beneficial effects of the present invention are: the present invention disclose it is a kind of with damping performance
Fabric is the three-decker for including the first base fabric, articulamentum and the second base fabric.The present invention has the fabric of damping performance using comb
Comb GB1, GB2 and GB3 weave the first base fabric, using sley bar GB4 and GB5 braiding articulamentum, using sley bar GB6 and GB7 braiding the
Two base fabrics.Spatially waveform, the first base fabric, the second base fabric have with intermediate connection interlayer respectively on the fabric substrate surface
There is hollow structure, there is good cushion performance, and can fast quick-recovery after compressive deformation.The high resilience that fabric has, can be
In pressurized process, generates flexible deformation and absorb energy, have excellent damping performance.
Detailed description of the invention
Fig. 1 is schematic perspective view of the invention;
Fig. 2 is warp knit damping textile plane schematic diagram: (a) being front;It (b) is row direction section;It (c) is reverse side;
Fig. 3 is the first base fabric warp knitting fabrics structure gauze pad motion diagram;
Fig. 4 is articulamentum institutional framework gauze pad motion diagram;
Fig. 5 is the second base fabric institutional framework gauze pad motion diagram.
Description of symbols: (the 1, first base fabric;2, articulamentum;3, the second base fabric;4, hollow region;5, the first mesh;6,
Second mesh).
Specific embodiment
It is clear to be more clear technical solution of the present invention, the present invention is made with reference to the accompanying drawings and detailed description
It is further to be described in detail.
In the description of the present invention, it is to be understood that, term " on ", "lower", "front", "rear", etc. the orientation of instructions or
Positional relationship is to be merely for convenience of description of the present invention and simplification of the description based on attached orientation or positional relationship shown in FIG. 1, without
It is that the structure of indication or suggestion meaning must have a particular orientation, be constructed and operated in a specific orientation, therefore cannot understand
For limitation of the present invention.
Embodiment 1
As shown in Figs. 1-2, a kind of fabric with damping performance of the present invention from top to bottom successively includes the first base fabric 1, connects
Connect layer 2 and the second base fabric 3;First base fabric 1, the second base fabric 3 are wave-like;The wave crest of first base fabric 1 is located above,
Breakpoint joint between the trough and articulamentum of first base fabric 1;The wave crest of second base fabric 3 is located below, the wave of the second base fabric 3
Breakpoint joint between paddy and articulamentum 2;The articulamentum 2 is that the braiding of high resiliency material is made.First base fabric 1 and articulamentum 2, the
The hollow region 4 of the arc shape formed between two base fabrics 3 and articulamentum 2 makes fabric of the present invention when thickness direction is by pressure, arc
Deformation occurs absorbs impact energy for the hollow region 4 of shape and elastomeric articulamentum 2, plays good absorbing shock performance.
First base fabric 1, the wavelength of the second base fabric 2 are equal;The wave of the wave crest of first base fabric 1 and the second base fabric 3
Paddy is corresponding.Heterogeneous Permutation between first base fabric 1, the second base fabric 3, and can further improve respectively with 2 breakpoint joint of articulamentum
The damping performance of fabric of the present invention.
First base fabric 1 and the second base fabric 3 are uniformly provided with several first mesh 5, several second mesh 6 respectively;First
Mesh 5 and the second mesh 6 are corresponding;First mesh 5 and the second mesh 6 are elongated shape;In the case of normality, the first mesh
5, the second mesh 6 through to length be 0.5-0.9cm, width 0.1-0.2cm.The first mesh 5, the second base of first base fabric 1
Second mesh 6 of cloth 3 can further improve the deformation range of the first base fabric 1, the second base fabric 3, improve the damping of fabric of the present invention
Cushion performance.When deformation occurs, the first mesh 5, the length of the second mesh 6, width also and then change fabric, the variation of the two
Adjustable range are as follows: length adjusting range can be 0.5-0.9cm, and width adjusting range can be 0.1-0.2cm.
First mesh 5 is located at the wave crest of the first base fabric 2;Second mesh 6 is located at the trough of the second base fabric 3.
First mesh 5, the corresponding setting of the second mesh 6, when fabric of the present invention receives impact, pressure, the first mesh 5,
The problems such as deformation discovery of second mesh 6 is consistent, the first base fabric 1,3 stress difference of the second base fabric is avoided to be pullled tearing hair
It is raw.
The vertical range of wave crest to the trough of first base fabric 1, the second base fabric 3 is 0.1-0.2cm;The articulamentum 2
With a thickness of 0.15-0.25cm.
Within the knowledge of those skilled in the art, can also make without departing from the inventive concept of the premise
Change out, such as change fabric thickness, changes fabric the first mesh 5, the length of the second mesh 6 and the first base fabric 1 and the second base fabric 3
Change over.
Embodiment 2
As shown in Figs. 1-5, a kind of weaving of the fabric with damping performance of the present invention, described has damping performance
Fabric sley bar is woven using seven;First base fabric 1 by reversely through flat lining latitude organizational composition, using sley bar GB1,
Sley bar GB2 and sley bar GB3 braiding;The articulamentum 2 is that variation warp sateen is mesh-structured, is woven using sley bar GB4 and sley bar GB5;
Second base fabric 3 is containing the free reversed warp plain stitch worn, using sley bar GB6 and sley bar GB7 material knitting.
Described 7 is as follows the band yarn yardage and drawing-in mode of sley bar:
The band yarn number of sley bar GB1 be (0-0/2-2) * 6//, drawing-in mode be 5 skies 1 wear;
The band yarn number of sley bar GB2 be (1-0/1-2) * 6//, drawing-in mode be 5 wear 1 sky;
The band yarn number of sley bar GB3 be (1-2/1-0) * 6//, drawing-in mode be 5 wear 1 sky;
The band yarn number of sley bar GB4 be (3-4-2-1) * 8+ (3-4-1-0) * 4//, drawing-in mode be 1 wear 11 sky;
The band yarn number of sley bar GB5 is (1-0-2-3) * 8+ (1-0-3-4) * 4, and drawing-in mode is that 11 skies 1 are worn;
The band yarn number of sley bar GB6 be (1-2/1-0) * 6//* 6//, drawing-in mode be 5 wear 1 sky;
The band yarn number of sley bar GB7 be (1-2/1-0) * 6//, drawing-in mode be 5 wear 1 sky.
Fabric of the present invention passes through above-mentioned band yarn code by sley bar GB1-GB7 by the double-needle bed raschels tricot machine such as RD7-EL type
Several and drawing-in mode is weaved, and can effectively be solved in existing warp knit three-decker, intermediate connecting layer and base fabric lack in elasticity
The problem of hollow structure reduces deformability in buffering course, constrains the raising of material damping performance.
The raw material of the sley bar GB1 and sley bar GB2 is POLYESTER HIGH ELASTIC YARN or polyamide fibre high stretch yarn, and monofilament yarn fineness is 6-
16tex;The sley bar GB3 raw material is POLYESTER HIGH ELASTIC YARN, and monofilament yarn fineness is 11.1-22.3tex.
The raw material of the sley bar GB4 and sley bar GB5 is POLYESTER HIGH ELASTIC YARN or polyamide fibre high stretch yarn, and monofilament yarn fineness is
11.1-22.3tex。
The raw material of the sley bar GB6 and sley bar GB7 is polyester monofilament, and the fineness of monofilament yarn is 6-16tex.
Different monofilament yarns is respectively adopted in first base fabric 1, articulamentum 2, the second base fabric 3, passes through fabric made of braiding
Middle layer: articulamentum 2 has high resilience, and the reply shrinkage stress after deformation pressing the first base fabric 1 and the second base fabric 3
It can fast quick-recovery after contracting deformation.
Certainly, the present invention can also have other various embodiments, without deviating from the spirit and substance of the present invention, ripe
Various corresponding changes and modifications, but these corresponding changes and modifications can be made according to the present invention by knowing those skilled in the art
All it should fall within the scope of protection of the appended claims of the present invention.
Claims (10)
1. a kind of fabric with damping performance, it is characterised in that: from top to bottom successively include the first base fabric, articulamentum and second
Base fabric;First base fabric, the second base fabric are wave-like;The wave crest of first base fabric is located above, the trough of the first base fabric
The breakpoint joint between articulamentum;The wave crest of second base fabric is located below, the trough of the second base fabric and the interruption of articulamentum
Point connection;The hollow region of the arc shape formed between first base fabric and articulamentum 2, the second base fabric and articulamentum;The connection
Layer is that the braiding of high resiliency material is made.
2. a kind of fabric with damping performance according to claim 1, it is characterised in that: first base fabric, second
The wavelength of base fabric is equal;The wave crest of first base fabric is corresponding with the trough of the second base fabric.
3. a kind of fabric with damping performance according to claim 2, it is characterised in that: first base fabric and second
Base fabric is uniformly provided with several first mesh, several second mesh respectively;First mesh and the second mesh are corresponding;First net
Hole and the second mesh are elongated shape;In the case of normality, the first mesh, the second mesh through to length be 0.5-0.9cm, width
For 0.1-0.2cm.
4. a kind of fabric with damping performance according to claim 3, it is characterised in that: first mesh is located at the
The wave crest of one base fabric;Second mesh is located at the trough of the second base fabric.
5. a kind of fabric with damping performance according to claim 3, it is characterised in that: first base fabric, second
The vertical range of the wave crest of base fabric to trough is 0.1-0.2cm;The articulamentum with a thickness of 0.15-0.25cm.
6. a kind of weaving of the fabric with damping performance, it is characterised in that described in any one of claim 1-5
The fabric with damping performance sley bar is woven using seven;First base fabric is by reversely through flat lining latitude group texture
At using sley bar GB1, sley bar GB2 and sley bar GB3 braiding;The articulamentum is that variation warp sateen is mesh-structured, using sley bar GB4
It is woven with sley bar GB5;Second base fabric is compiled containing the free reversed warp plain stitch worn using sley bar GB6 and sley bar GB7 raw material
It knits.
7. a kind of weaving of fabric with damping performance according to claim 6, it is characterised in that: described 7
The band yarn yardage and drawing-in mode of sley bar are as follows:
The band yarn number of sley bar GB1 be (0-0/2-2) * 6//, drawing-in mode be 5 skies 1 wear;
The band yarn number of sley bar GB2 be (1-0/1-2) * 6//, drawing-in mode be 5 wear 1 sky;
The band yarn number of sley bar GB3 be (1-2/1-0) * 6//, drawing-in mode be 5 wear 1 sky;
The band yarn number of sley bar GB4 be (3-4-2-1) * 8+ (3-4-1-0) * 4//, drawing-in mode be 1 wear 11 sky;
The band yarn number of sley bar GB5 is (1-0-2-3) * 8+ (1-0-3-4) * 4, and drawing-in mode is that 11 skies 1 are worn;
The band yarn number of sley bar GB6 be (1-2/1-0) * 6//* 6//, drawing-in mode be 5 wear 1 sky;
The band yarn number of sley bar GB7 be (1-2/1-0) * 6//, drawing-in mode be 5 wear 1 sky.
8. a kind of weaving of fabric with damping performance according to claim 6, it is characterised in that: the sley bar
The raw material of GB1 and sley bar GB2 are POLYESTER HIGH ELASTIC YARN or polyamide fibre high stretch yarn, and monofilament yarn fineness is 6-16tex;The sley bar GB3
Raw material is POLYESTER HIGH ELASTIC YARN, and monofilament yarn fineness is 11.1-22.3tex.
9. a kind of weaving of fabric with damping performance according to claim 6, it is characterised in that: the sley bar
The raw material of GB4 and sley bar GB5 are POLYESTER HIGH ELASTIC YARN or polyamide fibre high stretch yarn, and monofilament yarn fineness is 11.1-22.3tex.
10. a kind of weaving of fabric with damping performance according to claim 6, it is characterised in that: the comb
The raw material of comb GB6 and sley bar GB7 are polyester monofilament, and the fineness of monofilament yarn is 6-16tex.