CN105017711A - Preparation method of POM plastic particles used for automobile fuel tank - Google Patents
Preparation method of POM plastic particles used for automobile fuel tank Download PDFInfo
- Publication number
- CN105017711A CN105017711A CN201510384450.XA CN201510384450A CN105017711A CN 105017711 A CN105017711 A CN 105017711A CN 201510384450 A CN201510384450 A CN 201510384450A CN 105017711 A CN105017711 A CN 105017711A
- Authority
- CN
- China
- Prior art keywords
- parts
- fuel tank
- preparation
- pom plastic
- vehicle
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a preparation method of POM plastic particles used for an automobile fuel tank, which comprises the following step: adding the components according to mass part in a feed mixer, uniformly mixing to obtain a main material; then adding an auxiliary agent, uniformly mixing to obtain a mixture; adding in a twin-screw extruder, wherein the screw speed is 400-450r/min, after uniformly mixing, performing fusion extrusion to obtain a granular mixture under 260-300 DEG C; and cooling the granular mixture and granulating to obtain the product. The preparation method has the advantages of simple production technology, convenient operation and low cost. The fuel tank product prepared by the plastic particles has the advantages of uniform wall thickness, good intensity, impact resistance and excellent falling performance, and can be used for long-term application under outdoor scurviness environment (severe cold, intense heat of summer and long-term bumpiness shock).
Description
Technical field
The invention belongs to polymeric material field, relate to a kind of preparation method of fuel tank of vehicle POM plastic particle.
Technical background
Engineering plastics can be made engineering materials and replace metal to manufacture the plastics of element part etc.The performance characteristics of engineering plastics is mainly:
(1) compared with general-purpose plastics, there is excellent heat-resisting and cold tolerance, good mechanical performance in temperature range widely, suitablely to use as structured material;
(2) erosion resistance is good, affected by environment less, has good weather resistance;
(3) compared with metallic substance, easily process, production efficiency is high, and can simplify procedures, cost saving;
(4) good dimensional stability and electrical insulating property is had;
(5) lightweight, specific tenacity is high, and has outstanding antifriction, wear resistance.
At present, engineering plastics are because of the stability of its excellence, good heat-resisting and chemical resistant properties and high strength, and Application Areas is extensive, and its demand maintains sustained and rapid growth.One of main application of engineering plastics is the application of alternative metals in various terminal industry.Particularly the environmental regulation of increasingly stringent requires automobile emissions reduction amount and improves fuel economy, and engineering plastics are just being widely used in automobile and carrier.
Along with the development of automotive industry, the application of engineering plastics also will be more and more extensive; Fuel tank of vehicle is one of function part and safety member important in trolley part, and traditional fuel tank metal makes, due to the singularity of intermetallic composite coating, shaping more difficult, and the intensity at soldered place is also low, and production qualification rate is lower.Relative to traditional metal fuel tank, Engineering Plastic Fuel Tank then has the following advantages: the molding processibility of (1) plastics is good, easy scale production; (2) plastics have fabulous chemical resistance, and plastic fuel tank has the erosion action the trouble of removing maintenance from of resisting water, dirt and other media; (3) weight of plastic fuel tank comparatively metal light, plastics relative density is only 1/8 ~ 1/7 of metal, so compared with the metal fuel tank of same volume, its weight can reduce greatly, thus is conducive to alleviating car weight, improves the speed of a motor vehicle, fuel saving; (4) plastic fuel tank freedom of design in configuration is large, and space availability ratio is high, can be processed into various complicated shape, is conducive to the space making full use of car body, thus can increase the weight-carrying capacity of fuel oil, improves the steaming range of automobile.So, use Engineering Plastic Fuel Tank to replace traditional metal fuel tank to be inevitable trend.Polyoxymethylene (POM) is that one uses engineering plastic resin widely.There is the title of " taking steel by force ", " supersteel " abroad.POM has the hardness of metalloid, intensity and rigidity, within the scope of very wide temperature and humidity, all have good self lubricity, good resistance to fatigue, and springiness, it also has good chemical-resistant in addition.The fuel tank of the automobile that can make of polyoxymethylene (POM).Therefore people add various filler or auxiliary agent carries out modification in engineering plastics, but many modified effects are unsatisfactory.For this reason, we set about from the formula of product, develop new H.D starting material, provide a kind of polyoxymethylene (POM) plastic pellet that can be used for obtained high performance plastic fuel tank.
Summary of the invention
The object of the invention is to for the deficiencies in the prior art, a kind of preparation method of fuel tank of vehicle POM plastic particle is provided.
The object of the invention is to be achieved through the following technical solutions: a kind of preparation method of fuel tank of vehicle POM plastic particle, said method comprising the steps of: (1) is by mass parts, by POM80-90 part, copolymer 1 6-19 part of modified phenylethylene and divinyl, atactic copolymerized polypropene 22-25 part, trichloroisocyanuric acid 3-8 part, diacetone alcohol 0.6-1 part, alumina-silicate ceramic fibre 15-17 part, vinyl acetate 2-3 part, rhodia 3-5 part, maleated rosin 20-26 part, nitrilotriacetic acid(NTA) 3-6 part, methylene-bis (2, 4-di-tert-butyl-phenyl) phosphoric acid ester oxyaluminum salt 2-5 part adds in mixer, major ingredient is obtained after mixing, (2) in step (1) gained major ingredient, add anti-aging agent 3-7 part, softening agent 3-6 part and dispersion agent 2-5 part, after mixing, obtain mixture, (3) add in twin screw extruder by step (2) gained mixture, screw speed is 400-450r/min, after mixing, melt extrudes and obtain particulate blend under 260 DEG C of-300 DEG C of temperature condition, (4) pelletizing after the cooling of step (3) gained particulate blend is split, to obtain final product.
Described anti-aging agent is zinc dibutyl dithiocarbamate or 2,6 di tert butyl 4 methyl phenol.
Described softening agent is glycerine, sorbyl alcohol, seminose or polyoxyethylene glycol.
Described dispersion agent is the one in polyethylene wax, oxidized polyethlene wax, polyamide wax.
The multipolymer of described modified phenylethylene and divinyl is obtained by following methods: by weight, the multipolymer of 7 parts of vinylbenzene and divinyl is scattered in 6 parts of ethyl acetate, add 1 part of titanate coupling agent, 2 parts of azobisformamide ABFAs, 3 parts of methyl iso-butyl ketone (MIBK), 5 parts of Viscotrol C propylene oxide polymers again, be warming up to 150 ~ 160 DEG C, be incubated 2 ~ 3 hours, let cool.
The present invention has following beneficial effect: it is simple that the present invention has production technique, and easy to operate, cost is lower.The fuel tank product wall thickness obtained by plastic pellet of the present invention is even, and intensity is good, shock resistance, and drop performance is excellent, can severe environment (severe cold, heat, for a long time jolt vibrations etc.) prolonged application out of doors.
Embodiment
embodiment 1
A kind of preparation method of fuel tank of vehicle POM plastic particle; preparation method comprises the following steps: (1) is by mass parts; the copolymer 16 parts of POM80 part, modified phenylethylene and divinyl, atactic copolymerized polypropene 22 parts, trichloroisocyanuric acid 3 parts, diacetone alcohol 0.6 part, alumina-silicate ceramic fibre 15 parts, vinyl acetate 2 parts, rhodia 3 parts, maleated rosin 20 parts, nitrilotriacetic acid(NTA) 3 parts, methylene-bis (2,4-di-tert-butyl-phenyl) phosphoric acid ester oxyaluminum salt 2 parts are added in mixer, after mixing, obtains major ingredient; (2) in step (1) gained major ingredient, add 3 parts, anti-aging agent, 3 parts, softening agent and dispersion agent 2 parts, after mixing, obtain mixture; (3) add in twin screw extruder by step (2) gained mixture, screw speed is 400-450r/min, after mixing, melt extrudes and obtain particulate blend under 260 DEG C of-300 DEG C of temperature condition; (4) pelletizing after the cooling of step (3) gained particulate blend is split, to obtain final product.
Described anti-aging agent is zinc dibutyl dithiocarbamate or 2,6 di tert butyl 4 methyl phenol.
Described softening agent is glycerine, sorbyl alcohol, seminose or polyoxyethylene glycol.
Described dispersion agent is the one in polyethylene wax, oxidized polyethlene wax, polyamide wax.
The multipolymer of described modified phenylethylene and divinyl is obtained by following methods: by weight, the multipolymer of 7 parts of vinylbenzene and divinyl is scattered in 6 parts of ethyl acetate, add 1 part of titanate coupling agent, 2 parts of azobisformamide ABFAs, 3 parts of methyl iso-butyl ketone (MIBK), 5 parts of Viscotrol C propylene oxide polymers again, be warming up to 150 ~ 160 DEG C, be incubated 2 ~ 3 hours, let cool.
embodiment 2
A kind of preparation method of fuel tank of vehicle POM plastic particle; preparation method comprises the following steps: (1) is by mass parts; the copolymer 19 parts of POM90 part, modified phenylethylene and divinyl, atactic copolymerized polypropene 25 parts, trichloroisocyanuric acid 8 parts, diacetone alcohol 1 part, alumina-silicate ceramic fibre 17 parts, vinyl acetate 3 parts, rhodia 5 parts, maleated rosin 26 parts, nitrilotriacetic acid(NTA) 6 parts, methylene-bis (2,4-di-tert-butyl-phenyl) phosphoric acid ester oxyaluminum salt 5 parts are added in mixer, after mixing, obtains major ingredient; (2) in step (1) gained major ingredient, add 7 parts, anti-aging agent, 6 parts, softening agent and dispersion agent 5 parts, after mixing, obtain mixture; (3) add in twin screw extruder by step (2) gained mixture, screw speed is 400-450r/min, after mixing, melt extrudes and obtain particulate blend under 260 DEG C of-300 DEG C of temperature condition; (4) pelletizing after the cooling of step (3) gained particulate blend is split, to obtain final product.
Described anti-aging agent is zinc dibutyl dithiocarbamate or 2,6 di tert butyl 4 methyl phenol.
Described softening agent is glycerine, sorbyl alcohol, seminose or polyoxyethylene glycol.
Described dispersion agent is the one in polyethylene wax, oxidized polyethlene wax, polyamide wax.
The multipolymer of described modified phenylethylene and divinyl is obtained by following methods: by weight, the multipolymer of 7 parts of vinylbenzene and divinyl is scattered in 6 parts of ethyl acetate, add 1 part of titanate coupling agent, 2 parts of azobisformamide ABFAs, 3 parts of methyl iso-butyl ketone (MIBK), 5 parts of Viscotrol C propylene oxide polymers again, be warming up to 150 ~ 160 DEG C, be incubated 2 ~ 3 hours, let cool.
embodiment 3
A kind of preparation method of fuel tank of vehicle POM plastic particle; preparation method comprises the following steps: (1) is by mass parts; the copolymer 17 parts of POM85 part, modified phenylethylene and divinyl, atactic copolymerized polypropene 23 parts, trichloroisocyanuric acid 5 parts, diacetone alcohol 0.8 part, alumina-silicate ceramic fibre 16 parts, vinyl acetate 2.5 parts, rhodia 4 parts, maleated rosin 23 parts, nitrilotriacetic acid(NTA) 5 parts, methylene-bis (2,4-di-tert-butyl-phenyl) phosphoric acid ester oxyaluminum salt 4 parts are added in mixer, after mixing, obtains major ingredient; (2) in step (1) gained major ingredient, add 5 parts, anti-aging agent, 4 parts, softening agent and dispersion agent 4 parts, after mixing, obtain mixture; (3) add in twin screw extruder by step (2) gained mixture, screw speed is 400-450r/min, after mixing, melt extrudes and obtain particulate blend under 260 DEG C of-300 DEG C of temperature condition; (4) pelletizing after the cooling of step (3) gained particulate blend is split, to obtain final product.
Described anti-aging agent is zinc dibutyl dithiocarbamate or 2,6 di tert butyl 4 methyl phenol.
Described softening agent is glycerine, sorbyl alcohol, seminose or polyoxyethylene glycol.
Described dispersion agent is the one in polyethylene wax, oxidized polyethlene wax, polyamide wax.
The multipolymer of described modified phenylethylene and divinyl is obtained by following methods: by weight, the multipolymer of 8 parts of vinylbenzene and divinyl is scattered in 6 parts of ethyl acetate, add 1 part of titanate coupling agent, 4 parts of azobisformamide ABFAs, 5 parts of methyl iso-butyl ketone (MIBK), 4 parts of Viscotrol C propylene oxide polymers again, be warming up to 150 ~ 160 DEG C, be incubated 2 ~ 3 hours, let cool.
The above, it is only preferred embodiment of the present invention, not any pro forma restriction is done to the present invention, although the present invention discloses as above with preferred embodiment, but and be not used to limit the present invention, any those skilled in the art, do not departing within the scope of technical solution of the present invention, make a little change when the technology contents of above-mentioned announcement can be utilized or be modified to the Equivalent embodiments of equivalent variations, in every case be the content not departing from technical solution of the present invention, according to any simple modification that technical spirit of the present invention is done above embodiment, equivalent variations and modification, all still belong in the scope of technical solution of the present invention.
Claims (5)
1. the fuel tank of vehicle preparation method of POM plastic particle, it is characterized in that, said method comprising the steps of: (1) is by mass parts, by POM80-90 part, copolymer 1 6-19 part of modified phenylethylene and divinyl, atactic copolymerized polypropene 22-25 part, trichloroisocyanuric acid 3-8 part, diacetone alcohol 0.6-1 part, alumina-silicate ceramic fibre 15-17 part, vinyl acetate 2-3 part, rhodia 3-5 part, maleated rosin 20-26 part, nitrilotriacetic acid(NTA) 3-6 part, methylene-bis (2, 4-di-tert-butyl-phenyl) phosphoric acid ester oxyaluminum salt 2-5 part adds in mixer, major ingredient is obtained after mixing, (2) in step (1) gained major ingredient, add anti-aging agent 3-7 part, softening agent 3-6 part and dispersion agent 2-5 part, after mixing, obtain mixture, (3) add in twin screw extruder by step (2) gained mixture, screw speed is 400-450r/min, after mixing, melt extrudes and obtain particulate blend under 260 DEG C of-300 DEG C of temperature condition, (4) pelletizing after the cooling of step (3) gained particulate blend is split, to obtain final product.
2. the preparation method of a kind of fuel tank of vehicle POM plastic particle according to claim 1, it is characterized in that, described anti-aging agent is zinc dibutyl dithiocarbamate or 2,6 di tert butyl 4 methyl phenol.
3. the preparation method of a kind of fuel tank of vehicle POM plastic particle according to claim 1, it is characterized in that, described softening agent is glycerine, sorbyl alcohol, seminose or polyoxyethylene glycol.
4. the preparation method of a kind of fuel tank of vehicle POM plastic particle according to claim 1, it is characterized in that, described dispersion agent is the one in polyethylene wax, oxidized polyethlene wax, polyamide wax.
5. the preparation method of a kind of fuel tank of vehicle POM plastic particle according to claim 1, it is characterized in that, the multipolymer of described modified phenylethylene and divinyl is obtained by following methods: by weight, the multipolymer of 7 parts of vinylbenzene and divinyl is scattered in 6 parts of ethyl acetate, add 1 part of titanate coupling agent, 2 parts of azobisformamide ABFAs, 3 parts of methyl iso-butyl ketone (MIBK), 5 parts of Viscotrol C propylene oxide polymers again, be warming up to 150 ~ 160 DEG C, be incubated 2 ~ 3 hours, let cool.