CN103182463A - Manufacturing method of metal rubber shock pad - Google Patents
Manufacturing method of metal rubber shock pad Download PDFInfo
- Publication number
- CN103182463A CN103182463A CN2013100711992A CN201310071199A CN103182463A CN 103182463 A CN103182463 A CN 103182463A CN 2013100711992 A CN2013100711992 A CN 2013100711992A CN 201310071199 A CN201310071199 A CN 201310071199A CN 103182463 A CN103182463 A CN 103182463A
- Authority
- CN
- China
- Prior art keywords
- metal
- rubber
- manufacturing
- woven wire
- metal wire
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a manufacturing method of a metal rubber shock pad, which comprises following steps: selecting metal wires, and making a net structure through a knitter; rolling metal wire net to ensure that lines are formed on the metal wire net; measuring the length of the metal wire net, and segmenting the metal wire net; making the metal wire net into a blank; and press molding the blank. The manufacturing method simplifies a plurality of procedures such as spiral wind manufacturing, constant pitch drawing and metal wire winding, greatly simplifies the manufacturing process of metal rubber, obviously improves the production efficiency, reduces procedures and time of manual work, improves stability of metal rubber products, reasonably utilizes the metal wires to an extreme, and reduces the heads of the metal wires during the manufacturing process of metal rubber.
Description
Technical field
The present invention relates to a kind of preparation method of metal-rubber beam.
Background technology
Belong to rubber technology and originate from phase at the beginning of the sixties in last century former Soviet Union, countries such as U.S. Germany all dabble to some extent.Along with development of modern industry, in high-end technical fields such as Aero-Space naval vessel, it is particularly outstanding that the influence of vibratory impulse shows.The existence of vibration influences the normal operation of various instrument and meters, has seriously reduced its reliability and service life, also makes naval vessel and aircraft be difficult to reach stealth effect.
Metal-rubber is to be twined by stainless steel metal wire, and being made through special process has flexible hardware as the rubber.Because characteristics such as metallic rubber vibration isolator has high-low temperature resistant, corrosion-resistant, anti-aging, radiation hardness, bearing capacity is strong, damping capacity good, density and porosity are adjustable.Compare with elastomeric material with other simple metal polyporous materials, have incomparable good characteristic.Therefore it is with a wide range of applications in every field.But metal-rubber beam manufacturing process complexity, the metal-rubber product from the wire to the reservation shape need carry out multiple tracks technology, uses under the manual efficient of finishing of traditional approach, can't realize automatic assembly line production, is difficult to provide requirement product on time.For the simple relatively product of shape, need a kind of more advantages of simplicity and high efficiency mode of production, in the case, it is very necessary developing a kind of new beam of metal-rubber efficiently manufacture method.
Summary of the invention
The object of the present invention is to provide a kind of preparation method of utilizing braider to make the metal-rubber beam.
The object of the present invention is achieved like this:
The preparation method of metal-rubber beam comprises the steps:
(1) chooses wire, make network structure by braider;
(2) roll extrusion woven wire makes woven wire form lines;
(4) measure woven wire length, with the woven wire intercept;
(3) woven wire is made blank;
(4) blank punch forming.
Blank can be stamped into circle, square, annular, counterbore.
Beneficial effect of the present invention is:
The present invention can simplify multiple working procedures such as the manufacturing, constant pitch stretching, wire winding of helical coil, and the preparation process of metal-rubber is simplified greatly, has obviously improved production efficiency.Reduce operation and the time of handwork, improved the stability of metal-rubber product, rationally utilized wire to the full extent, reduced silk head wiry in the metal-rubber manufacturing process
Description of drawings
Fig. 1 woven wire knit unit section construction figure;
Fig. 2 circular hollow metal-rubber;
Fig. 3 net metal silk;
Fig. 4 woven wire blank winding method.
The specific embodiment
For example the present invention is done more detailed description below in conjunction with accompanying drawing.
This method can reduce the multiple tracks technology that metal-rubber is made, and finishes Related product fast.Use the wire of the optional majority kind of the metal-rubber beam different-diameter that this mode makes, its manufacture method is: a. chooses the wire of suitable diameter, and it is netted to utilize braider to make; B. measure the wire netting of appropriate length then, make its quality reach prospective quality; C. the roll extrusion woven wire makes woven wire form certain lines; D. woven wire is made blank; E. with the blank punch forming.
The metal-rubber cushion blocking that the present invention makes is compared with the metal-rubber beam of traditional method for making, gap is little on performance, and the manufacturing of woven wire can substitute multiple working procedures such as the manufacturing, constant pitch stretching, wire winding of helical coil, the preparation process of metal-rubber is simplified greatly, obviously improved production efficiency.Utilize the performance of the metal-rubber cushion blocking that braider makes to depend on characteristic with woven wire to a great extent.Problems such as woven wire adopts the braider manufacturing, and mechanization production can guarantee the uniformity that woven wire weaves in manufacturing process, and it is uneven the woven wire size can not occur, and the centre is leaky.The present invention compares with traditional manufacturing technique, has reduced operation and the time of handwork.The handwork quality is uneven, can't guarantee the stability of product, and the test of its performance is had very big influence.Therefore, the present invention can improve the stability of metal-rubber product.In addition, the metal-rubber manufacture method that the present invention proposes can rationally be utilized wire to the full extent, reduces silk head wiry in the metal-rubber manufacturing process.In the braiding process of woven wire, use an one metal wire to finish, improved the performance of metal-rubber to a certain extent.The metal-rubber of different shapes such as the metal-rubber manufacture method that the present invention proposes can be circular, square according to the demand preparation of actual condition, annular, counterbore, can satisfy the appearance and size requirement in fields such as machinery, aviation, naval vessels, have applicability very widely.
The present invention proposes a kind of new type of metal rubber manufacture method, unique technology makes the industrialization of metal-rubber become possibility: the innovation and application of woven wire has reduced hand-built difference to the full extent, make the stable performance of metal-rubber beam easier, the manufacturing process of easier curing metal Rubber shock-absorbing pad; The proposition of roll extrusion woven wire makes the profile of metal-rubber beam obtain beautifying, make metal-rubber in punching course, can carry out moulding along the lines of roll extrusion, improved the woven wire metal-rubber in the stability in punching press stage, and this measure can make product be improved in performances such as compression, vibration dampings; Change material, the geomery of metal-rubber beam, can make the metal-rubber beam have different damping properties, be conducive to form series of products, satisfy the demand of different operating modes.Using the metal-rubber beam of this kind method manufacturing to produce in enormous quantities, is the prerequisite that metal-rubber is carried out industrialization.The present invention makes the making of metal-rubber beam become easier, easy to operate.
The specific embodiment one: in conjunction with shown in Figure 1, wire weaves by the crochet hook (1) of braider, and the continuous unit coil forms to a direction string cover, finally can form the woven wire of endless.Then woven wire is carried out cutting at length direction, make its quality reach prospective quality.The woven wire that cuts is carried out roll extrusion, coiling back formation blank, at last by the mould punch forming.In the braiding process, the bore width of braider has determined the width of woven wire, and finally has influence on the altitude range of metal-rubber beam.
The specific embodiment two: in conjunction with shown in Figure 2, the cross section of metal-rubber beam is circular and with holes in the present embodiment, and the wire of making beam is stainless steel wire.
Claims (2)
1. the preparation method of a metal-rubber beam is characterized in that, comprises the steps:
(1) chooses wire, make network structure by braider;
(2) roll extrusion woven wire makes woven wire form lines;
(4) measure woven wire length, with the woven wire intercept;
(3) woven wire is made blank;
(4) blank punch forming.
2. the preparation method of a kind of metal-rubber beam according to claim 1 is characterized in that, described blank can be stamped into circle, square, annular, counterbore.